C95800 Alpha Nickel Aluminum Bronze

Shapes Available

C95800 Alpha Nickel Aluminum Bronze

Typical Uses for C95800 Alpha Nickel Aluminum Bronze:

C95800 offers superior salt water corrosion resistance. It also is resistant to cavitation and erosion. Along with the advantage of pressure tightness, this high strength alloy is excellent for welding and is available in many forms at a lower cost to you.

Cast ASTM: B271, B505, B148 Military/AMS: MIL-B-24480 Other: ABS - 4

Common Applications:

Piping for Vertical Pump Columns
Firefighting and Fire Suppression Systems
Seawater Lift Pumps
Piping Layout, Flanges and Fittings
Discharge Elbows
Cooling Loops for Power Plants
Bronze Valve Bodies
Piping Systems
Desalination Equipment
Tube Sheets
Circulating Pumps and Pump Shafts
Fasteners, Hardware for Cooling towers

Request a Quote

Al Cu Fe Pb Mn Ni Si
Min/Max 8.5-9.5 79.0 min 3.5-4.5 0.03 .8-1.5 4.0-5.0 0.1
Nominals 9.0000 81.0000 4.0000 - 1.0000 4.5000 -
Product Type Temper Type
Centrifugal ASTM B271, SAE J462, J461
Continuous ASTM B505, SAE J461, J462
Ingot ASTM B30
Precision ASTM B806
Sand ASTM B148, B763, MILITARY MIL-B-24480, SAE J461, J462
Temper Sect. Size Cold Work Type Min Temp Tensile Strength YS
0.5% EUL
Elong. RH
B
RH
C
RH
F
RH
30T
VH
500
BH
500
BH
3000
Shear
Strgth
Fatigue
Strgth
Izod
Impact
Strgth
- in. % - F ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb
- mm. - - C MPa MPa - - - - - - - - MPa MPa J
M02 68 85 35 - - - - - - - - - -
M02 0 SMIN 20 585 240 15 - - - - - - - - - 0
As Continous Cast
M07 68 85 35 - - - - - - - - - -
M07 0 SMIN 20 586 241 18 - - - - - - - - - 0
As Permanent Mold Cast
M05 68 90 40 - - - - - - - - - -
M05 0 SMIN 20 620 275 15 - - - - - - - - - 0
M05 68 96 52 - - - - - - - - - -
M05 0 TYP 20 660 360 17 88 - - - - - - - - 0
As Sand Cast
M01 68 85 35 - - - - - - - - - -
M01 0 SMIN 20 585 240 15 - - - - - - - - - 0
M01 68 95 38 - - - - - - - 159 58 31 20
M01 0 TYP 20 655 262 25 - - - - - - 159 400 214 27
Product Property US Customary Metric
Coefficient of Thermal Expansion 9.0 . 10-6 per oF (68-572 F) 16.2 . 10-6 per oC (20-300 C)
Density 0.276 lb/in3 at 68 F 7.64 gm/cm3 @ 20 C
Electrical Conductivity 7 %IACS @ 68 F 0.041 MegaSiemens/cm @ 20 C
Electrical Resistivity 146.7 ohms-cmil/ft @ 68 F 34.39 microhm-cm @ 20 C
Information not available on website
Magnetic Permeability 1.05 1.05
Melting Point - Liquidus 1940 F 1060 C
Melting Point - Solidus 1910 F 1043 C
Modulas of Elasticity in Tension 16500 ksi 114000 MPa
Poisson's Ratio 0.32 0.32
Specific Gravity 7.64 7.64
Specific Heat Capacity 0.105 Btu/lb/oF at 68 F 440.0 J/kg . oK at 293 K
Thermal Conductivity 20.8 Btu . ft/(hr . ft2 . oF)at 68F 36.0 W/m . oK at 20 C
Joining Technique Suitability
Brazing Fair
Coated Metal Arc Welding Good
Gas Shielded Arc Welding Good
Machinability Rating 50
Oxyacetylene Welding Not Recommended
Soldering Good
End Product Specification
Centrifugal ASTM B271, SAE J462, J461
Continuous ASTM B505, SAE J461, J462
Ingot ASTM B30
Precision ASTM B806
Sand ASTM B148, B763, MILITARY MIL-B-24480, SAE J461, J462