USA CorporateCuTe / C14500
Mechanical
| Temper | Section Size |
Cold Work |
Typ/ Min |
Temp | Tensile Strength |
Yield Strength (0.5% ext. under load) |
Yield Strength (0.2% offset) |
Yield Strength (0.05% offset) |
El | Rockwell Hardness |
Vickens Hard. |
Brinell Hard. |
Shear Strength |
*Fatigue Strength |
Izod Impact Strength |
||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| in. | % | F | ksi | ksi | ksi | ksi | % | B | C | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb | ||
| mm. | C | MPa | MPa | MPa | MPa | MPa | MPa | J | |||||||||||
| Rod | |||||||||||||||||||
| H02 | 2 | 15 | TYP | 68 | 42 | 39 | - | - | 35 | - | - | - | - | - | - | - | 25 | - | 0.0 |
| 51 | 20 | 290 | 269 | - | - | 35 | - | - | - | - | - | - | - | 172 | - | 0.0 | |||
| OS015 | 0.5 | 0 | TYP | 68 | 33 | 11 | - | - | 46 | - | - | 43 | - | - | - | - | 22 | - | 0.0 |
| 12.7 | 20 | 228 | 76 | - | - | 46 | - | - | 43 | - | - | - | - | 152 | - | 0.0 | |||
| H00 | 0.5 | 6 | TYP | 68 | 38 | 30 | - | - | 26 | 36 | - | - | 44 | - | - | - | 25 | - | 0.0 |
| 12.7 | 20 | 262 | 207 | - | - | 26 | 36 | - | - | 44 | - | - | - | 172 | - | 0.0 | |||
| Wire | |||||||||||||||||||
| H00 | 0.08 | 0 | TYP | 68 | 38 | 30 | - | - | 20 | - | - | - | - | - | - | - | 25 | - | 0.0 |
| 2 | 20 | 262 | 207 | - | - | 20 | - | - | - | - | - | - | - | 172 | - | 0.0 | |||
| Rod | |||||||||||||||||||
| H04 | 0.5 | 35 | TYP | 68 | 48 | 44 | - | - | 15 | 48 | - | - | - | - | - | - | 27 | - | 0.0 |
| 12.7 | 20 | 331 | 303 | - | - | 15 | 48 | - | - | - | - | - | - | 186 | - | 0.0 | |||
| H02 | 0.25 | 20 | TYP | 68 | - | - | - | - | 18 | 43 | - | - | - | - | - | - | 26 | - | 0.0 |
| 6.35 | 20 | - | - | - | - | 18 | 43 | - | - | - | - | - | - | 179 | - | 0.0 | |||
| H02 | .25 | 0 | SMIN | 68 | 38 | 30 | - | - | 12 | - | - | - | - | - | - | - | - | - | 0.0 |
| 6.35 | 20 | 260 | 205 | - | - | 12 | - | - | - | - | - | - | - | - | - | 0.0 | |||
| OS050 | 1 | 0 | TYP | 68 | 32 | 10 | - | - | 50 | - | - | 40 | - | - | - | - | 22 | - | 0.0 |
| 25.4 | 20 | 221 | 69 | - | - | 50 | - | - | 40 | - | - | - | - | 152 | - | 0.0 | |||
| H04 | 1 | 35 | TYP | 68 | 48 | 44 | - | - | 20 | 48 | - | - | - | - | - | - | 27 | - | 0.0 |
| 25.4 | 20 | 331 | 303 | - | - | 20 | 48 | - | - | - | - | - | - | 186 | - | 0.0 | |||
| H02 | 0.5 | 20 | TYP | 68 | 43 | 40 | - | - | 20 | 43 | - | - | 50 | - | - | - | 26 | - | 0.0 |
| 12.7 | 20 | 296 | 276 | - | - | 20 | 43 | - | - | 50 | - | - | - | 179 | - | 0.0 | |||
| H02 | 0.25 | 20 | SMIN | 68 | 38 | 40 | - | - | - | - | - | - | - | - | - | - | - | - | 0.0 |
| 6.35 | 20 | 296 | 276 | - | - | - | - | - | - | - | - | - | - | - | - | 0.0 | |||
| Tube | |||||||||||||||||||
| H55 | 0.065 | 15 | TYP | 68 | 40 | 32 | - | - | 20 | 35 | - | - | - | - | - | - | 24 | - | 0.0 |
| 1.65 | 20 | 276 | 221 | - | - | 20 | 35 | - | - | - | - | - | - | 165 | - | 0.0 | |||
| Rod | |||||||||||||||||||
| H02 | 1 | 20 | TYP | 68 | 42 | 40 | - | - | 25 | 42 | - | - | - | - | - | - | 25 | - | 0.0 |
| 25.4 | 20 | 290 | 276 | - | - | 25 | 42 | - | - | - | - | - | - | 172 | - | 0.0 | |||
| Wire | |||||||||||||||||||
| OS035 | 0.08 | 0 | TYP | 68 | 33 | 11 | - | - | 40 | - | - | - | - | - | - | - | 22 | - | 0.0 |
| 2 | 20 | 228 | 76 | - | - | 40 | - | - | - | - | - | - | - | 152 | - | 0.0 | |||
| H04 | 0.08 | 0 | TYP | 68 | 56 | 51 | - | - | 3 | - | - | - | - | - | - | - | 30 | - | 0.0 |
| 2 | 20 | 386 | 352 | - | - | 3 | - | - | - | - | - | - | - | 207 | - | 0.0 | |||
| Rod | |||||||||||||||||||
| H02 | .0625 | 0 | SMIN | 68 | 38 | 30 | - | - | 8 | - | - | - | - | - | - | - | - | - | 0.0 |
| 1.6 | 20 | 260 | 205 | - | - | 8 | - | - | - | - | - | - | - | - | - | 0.0 | |||
| H04 | 0.25 | 45 | TYP | 68 | 53 | 49 | - | - | 10 | 54 | - | - | - | - | - | - | 29 | - | 0.0 |
| 6.35 | 20 | 365 | 338 | - | - | 10 | 54 | - | - | - | - | - | - | 200 | - | 0.0 | |||
| Wire | |||||||||||||||||||
| H02 | 0.08 | 0 | TYP | 68 | 51 | 41 | - | - | 6 | - | - | - | - | - | - | - | 27 | - | 0.0 |
| 2 | 20 | 352 | 283 | - | - | 6 | - | - | - | - | - | - | - | 186 | - | 0.0 | |||
| Tube | |||||||||||||||||||
| OS050 | 0.065 | 0 | TYP | 68 | 32 | 10 | - | - | 40 | - | - | 40 | - | - | - | - | 22 | - | 0.0 |
| 1.65 | 20 | 221 | 69 | - | - | 40 | - | - | 40 | - | - | - | - | 152 | - | 0.0 | |||
*Fatigue Strength: 100 x 10 6cycles, unless indicated as [N]X 106.
Tempers Most Commonly Used
| Flat Products | |
| BAR, DRAWN | H02 |
| Other | |
| ROD | H00, H01, H02, H04, OS015, OS035, OS050 |
| TUBE | H55, H58, O60 |
| WIRE | H00, H01, H04, OS035 |