USA CorporateCuSn10 / C52400
Physical
| US Customary | Metric | |
|---|---|---|
| Melting Point - Liquidus | 1830 F | 999 C |
| Melting Point - Solidus | 1550 F | 843 C |
| Density | 0.317 lb/in3 at 68 F | 8.77 gm/cm3 @ 20 C |
| Specific Gravity | 8.78 | 8.78 |
| Electrical Resistivity | 94.3 ohms-cmil/ft @ 68 F | 15.68 microhm-cm @ 20 C |
| Electrical Conductivity | 11 %IACS @ 68 F | 0.064 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 29.0 Btu · ft/(hr · ft2·oF)at 68F | 50.2 W/m · oK at 20 C |
| Coefficient of Thermal Expansion | 10.2 ·10-6 per oF (68-572 F) | 18.4 ·10-6 per oC (20-300 C) |
| Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg/ · oK at 293 K |
| Modulas of Elasticity in Tension | 16000 ksi | 110000 MPa |
| Modulas of Rigidity | 6000 ksi | 41370 MPa |
Common Fabrication Processes
Bending, Blanking, Forming, Shearing
Fabrication Properties
| Joining Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Fair |
| Spot Weld | Good |
| Seam Weld | Fair |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Machinability Rating | 20 |