Temper	Section Size	Cold Work	Typ/ Min	Temp	Tensile Strength	Yield Strength (0.5% ext. under load)	Yield Strength (0.2% offset)	Yield Strength (0.05% offset)	El	Rockwell Hardness				Vickens Hard.	Brinell Hard.		Shear Strength	*Fatigue Strength	Izod Impact Strength
	in.	%		F	ksi	ksi	ksi	ksi	%	B	C	F	30T	500	500	3000	ksi	ksi	ft-lb
	mm.			C	MPa	MPa	MPa	MPa									MPa	MPa	J
Rod
OS035	1	0	TYP	68	40	15	-	-	50	-	-	55	-	-	-	-	-	-	0.0
	25.4			20	276	103	-	-	50	-	-	55	-	-	-	-	-	-	0.0
Wire
H06	0.08	0	TYP	68	105	71	-	-	10	-	-	-	-	-	-	-	53	28	0.0
	2			20	724	490	-	-	10	-	-	-	-	-	-	-	365	193	0.0
Tube
H80	0.0	35	TYP	68	65	40	-	-	20	75	-	-	67	-	-	-	-	-	0.0
	0.0			20	448	276	-	-	20	75	-	-	67	-	-	-	-	-	0.0
Rod
H06	1	50	TYP	68	90	67	-	-	12	90	-	-	-	-	-	-	50	-	0.0
	25.4			20	621	462	-	-	12	90	-	-	-	-	-	-	345	-	0.0
Wire
H04	0.44	60	TYP	68	95	-	-	-	12	-	-	-	-	-	-	-	-	-	0.0
	11			20	655	-	-	-	12	-	-	-	-	-	-	-	-	-	0.0
H01	0.08	0	TYP	68	65	50	-	-	25	-	-	-	-	-	-	-	40	-	0.0
	2			20	448	345	-	-	25	-	-	-	-	-	-	-	276	-	0.0
H00	0.08	0	TYP	68	55	40	-	-	40	-	-	-	-	-	-	-	36	-	0.0
	2			20	379	276	-	-	40	-	-	-	-	-	-	-	248	-	0.0
Rod
H04	1	36	TYP	68	70	55	-	-	15	80	-	-	-	-	-	-	45	-	0.0
	25.4			20	483	379	-	-	15	80	-	-	-	-	-	-	310	-	0.0
Wire
H02	0.44	37	TYP	68	80	-	-	-	20	-	-	-	-	-	-	-	-	-	0.0
	11			20	552	-	-	-	20	-	-	-	-	-	-	-	-	-	0.0
Tube
OS015	0.065	0	TYP	68	45	20	-	-	55	-	-	68	-	-	-	-	-	-	0.0
	1.8			20	310	138	-	-	55	-	-	68	-	-	-	-	-	-	0.0
Wire
H01	0.44	21	TYP	68	63	-	-	-	30	-	-	-	-	-	-	-	-	-	0.0
	11			20	434	-	-	-	30	-	-	-	-	-	-	-	-	-	0.0
H04	0.08	0	TYP	68	100	70	-	-	11	-	-	-	-	-	-	-	50	25	0.0
	2			20	689	483	-	-	11	-	-	-	-	-	-	-	345	172	0.0
H02	0.08	0	TYP	68	80	63	-	-	15	-	-	-	-	-	-	-	45	-	0.0
	2			20	552	434	-	-	15	-	-	-	-	-	-	-	310	-	0.0