Physical Properties
C92200 Leaded Tin Bronze "Navy M"
| US Customary | Metric | |
|---|---|---|
| Melting Point - Liquidus | 1810 F | 988 C |
| Melting Point - Solidus | 1518 F | 826 C |
| Incipient Melting | 600 F | 315 C |
| Density | 0.312 lb/in3 at 68 F | 8.64 gm/cm3 @ 20 C |
| Specific Gravity | 8.64 | 8.64 |
| Electrical Resistivity | 72.5 ohms-cmil/ft @ 68 F | 12.0 microhm-cm @ 20 C |
| Electrical Conductivity | 14 %IACS @ 68 F | 0.083 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 40.2 Btu · ft/(hr · ft2·oF)at 68F | 69.6 W/m · oK at 20 C |
| Coefficient of Thermal Expansion | 10.0 ·10-6 per oF (68-572 F) | 18.0 ·10-6 per oC (20-200 C) |
| Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg · oK at 293 K |
| Modulas of Elasticity in Tension | 14000 ksi | 96500 MPa |
| Magnetic Permeability | 1.0 | 1.0 |
Common Fabrication Processes
Casting
Fabrication Properties
| Joining Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Excellent |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Machinability Rating | 42 |