C61000 Aluminum Bronze

Typical Uses for C61000 Aluminum Bronze

Architecture: Decorative Applications

Fasteners: Bolts

Industrial: Tie Rods, Welding Wire, Shafts, Pump Parts, Overlay on Steel for Wearing Surface

Specifications

End Product Specification
Bar FEDERAL QQ-C-450
Electrode, Welding AWS A5.7
MILITARY MIL-E-23765/3
Plate FEDERAL QQ-C-450
Sheet FEDERAL QQ-C-450
Strip FEDERAL QQ-C-450

Cu Al Fe Pb Si Zn
Min./Max. Rem. 6.0-8.5 .50 .02 .10 .20
Nominal 92.0 8.0 - - - -
Flat Products -
BAR, ROLLED H04, O60
PLATE H04, O60
SHEET H04, O60
STRIP, ROLLED H04, O60
Temper Sect. Size Cold Work Type Min Temp Tensile Strength YS
0.05% UL
YS
0.02% Offset
YS
0.005% Offset
Elong. RH
B
RH
C
RH
F
RH
30T
VH
500
BH
500
BH
3000
Shear
Strgth
Fatigue
Strgth
Izod
Impact
Strgth
- in. % - F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb
- mm. - - C MPa MPa MPa MPa - - - - - - - - MPa MPa J
Sheet
O60 1 0 TYP 68 52 17 - - 45 60 - - - - - - - - 0.0
25.4 20 359 117 - - 45 60 - - - - - - - - 0.0
Plate
H04 1 0 TYP 68 60 27 - - 30 85 - - - - - - - - 0.0
25.4 20 414 186 - - 30 85 - - - - - - - - 0.0
H04 0.5 0 TYP 68 65 24 - - 30 85 - - - - - - - - 0.0
12.2 20 448 165 - - 30 85 - - - - - - - - 0.0
Strip
H04 0.5 0 TYP 68 65 24 - - 30 85 - - - - - - - - 0.0
12.2 20 448 165 - - 30 85 - - - - - - - - 0.0
Sheet
H04 0.5 0 TYP 68 65 24 - - 30 85 - - - - - - - - 0.0
12.2 20 448 165 - - 30 85 - - - - - - - - 0.0
Strip
O60 1 0 TYP 68 52 17 - - 45 60 - - - - - - - - 0.0
25.4 20 359 117 - - 45 60 - - - - - - - - 0.0
Plate
O60 1 0 TYP 68 52 17 - - 45 60 - - - - - - - - 0.0
25.4 20 359 117 - - 45 60 - - - - - - - - 0.0
Product Property US Customary Metric
Melting Point - Liquidus 1905 F 1041 C
Density 0.281 lb/in3 at 68 F 7.78 gm/cm3 @ 20 C
Electrical Conductivity 7.780 7.78
Electrical Resistivity 69.20 ohms-cmil/ft @ 68 F 11.5 microhm-cm @ 20 C
Melting Point Liquid US 15 F 15 %IACS @ 68 F 0.088 MegaSiemens/cm @ 20 C
Melting Point Solid US 40 Btu . ft/(hr . ft2oF)at 68F 69.2 W/m . oK at 20 C
Modulas of Elasticity in Tension 9.90 . 10-6 per oF (68-572 F) 17.8 . 10-6 per oC (20-300 C)
Modulas of Rigidity 0.090 Btu/lb/oF at 68 F 377.1 J/kg . oK at 293 K
Specific Gravity 17000 ksi 117000 MPa
Specific Heat Capacity 6400 ksi 44130 MPa
Joining Technique Suitability
Soldering Fair
Brazing Not Recommended
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Good
Spot Weld Good
Seam Weld Fair
Butt Weld Good
Capacity for Being Cold Worked Good
Capacity for Being Hot Formed Good
Forgeability Rating 70
Machinability Rating 20