CHEMICAL COMPOSITION
|
Al |
Sb |
Cu |
Fe |
Pb |
Ni |
P |
Si |
S |
Sn |
Zn |
|
Min/Max
|
0.005 |
0.25 |
85.0 - 88.0 |
0.3 |
1.0 - 1.5 |
0.80 - 1.5 |
0.3 |
0.005 |
0.05 |
10.0 - 12.0 |
0.5 |
|
Nominals
|
- |
- |
86.5000 |
- |
1.3000 |
1.2000 |
- |
- |
- |
11.0000 |
- |
TEMPER
| Product Type |
Temper Type |
| Continuous |
ASTM B505, SAE J461, J462 |
| Ingot |
ASTM B30 |
| Sand |
SAE J462, J461 |
MECHANICAL PROPERTIES
| Temper |
Sect. Size |
Cold Work |
Type Min |
Temp |
Tensile Strength |
YS 0.05% UL
|
YS 0.02% Offset
|
YS 0.005% Offset
|
Elong. |
RH B
|
RH C
|
RH F
|
RH 30T
|
VH 500
|
BH 500
|
BH 3000
|
Shear Strgth
|
Fatigue Strgth
|
Izod Impact Strgth
|
| - |
in. |
% |
- |
F |
ksi |
ksi |
ksi |
ksi |
% |
B |
C |
F |
30T |
500 |
500 |
3000 |
ksi |
ksi |
ft-lb |
| - |
mm. |
- |
- |
C |
MPa |
MPa |
MPa |
MPa |
- |
- |
- |
- |
- |
- |
- |
- |
MPa |
MPa |
J |
| As Continous Cast |
| M07 |
|
|
|
68 |
40 |
24 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
|
| M07 |
|
0 |
SMIN |
20 |
276 |
165 |
- |
- |
10 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
0 |
| As Sand Cast |
| M01 |
|
|
|
68 |
44 |
20 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
|
| M01 |
|
0 |
TYP |
20 |
303 |
138 |
- |
- |
20 |
- |
- |
- |
- |
- |
80 |
- |
- |
- |
0 |
PHYSICAL PROPERTIES
| Product Property |
US Customary |
Metric |
| Density |
0.317 lb/in3 at 68 F |
8.7 gm/cm3 @ 20 C |
| Incipient Melting |
600 oF |
316 C |
| Modulas of Elasticity in Tension |
16000 ksi |
110000 MPa |
| Specific Gravity |
8.7 |
8.7 |
| Specific Heat Capacity |
0.09 Btu/lb/oF at 68 F |
377.1 J/kg · oK at 293 K |
FABRICATION
| Joining Technique |
Suitability |
| Brazing |
Good |
| Coated Metal Arc Welding |
Not Recommended |
| Gas Shielded Arc Welding |
Not Recommended |
| Machinability Rating |
30 |
| Oxyacetylene Welding |
Not Recommended |
| Soldering |
Excellent |
SPECIFICATIONS
| End Product |
Specification |
| Continuous |
ASTM B505, SAE J461, J462 |
| Ingot |
ASTM B30 |
| Sand |
SAE J462, J461 |
|