C62400 Aluminum Bronze

C62400 Aluminum Bronze
ASTM B150

C62300 and C62400 aluminum bronze applications include valve and pump components for industrial process streams, as well as for marine equipment, high strength fasteners and pole line hardware.

TYPICAL USES FOR C62400 ALUMINUM BRONZE

FASTENERS: Nuts
INDUSTRIAL: Support Bushings, Valve Balls, Welding Wire, Wear Plates, Tie Rods, Gears, Cams, Drift Pins, Hydraulic Bushings, Bushings

<<< SEE SIZES & SPECS BELOW >>

CHEMICAL COMPOSITION

	Al	Cu	Fe	Mn	Si	Sn
Min/Max	10.0 - 11.5	Rem	2.0 - 4.5	0.3	0.25	0.2
Nominals	11.0000	86.0000	3.0000	-	-	-

TEMPER

Product Type	Temper Type
Forgings	SAE J463, J461
Rod	ASTM B150
Rod, Welding	AWS A5.7

MECHANICAL PROPERTIES

Temper	Sect. Size	Cold Work	Type Min	Temp	Tensile Strength	YS 0.05% UL	YS 0.02% Offset	YS 0.005% Offset	Elong.	RH B	RH C	RH F	RH 30T	VH 500	BH 500	BH 3000	Shear Strgth	Fatigue Strgth	Izod Impact Strgth
-	in.	%	-	F	ksi	ksi	ksi	ksi	%	B	C	F	30T	500	500	3000	ksi	ksi	ft-lb
-	mm.	-	-	C	MPa	MPa	MPa	MPa	-	-	-	-	-	-	-	-	MPa	MPa	J
BAR
M30	2.99			68	90	40	-	-	-	-	-	-	-	-	-	-	-	-
M30	76	0	TYP	20	621	276	-	-	18	87	-	-	-	-	-	-	-	-	0
O50	2.01			68	93	45	-	-	-	-	-	-	-	-	-	-	-	-
O50	51	0	TYP	20	641	310	-	-	14	91	-	-	-	-	-	-	-	-	0
O50	1			68	100	50	-	-	-	-	-	-	-	-	-	-	-	-
O50	25.4	0	TYP	20	689	345	-	-	14	92	-	-	-	-	-	-	-	-	0
ROD
H02	1			68	105	52	-	-	-	-	-	-	-	-	-	-	65	36
H02	25.4	10	TYP	20	724	359	-	-	14	92	-	-	-	-	-	-	448	248	0
H02	2.99			68	95	47	-	-	-	-	-	-	-	-	-	-	60	34
H02	76	0	TYP	20	655	324	-	-	14	91	-	-	-	-	-	-	414	234	0
M30	4.02			68	90	40	-	-	-	-	-	-	-	-	-	-	58	32
M30	102	0	TYP	20	621	276	-	-	18	87	-	-	-	-	-	-	400	221	0
H02	2.01			68	95	48	-	-	-	-	-	-	-	-	-	-	62	35
H02	51			20	655	331	-	-	14	92	-	-	-	-	-	-	427	241	0
HR50	0.47				95	45	-	-	-	-	-	-	-	-	-	-	-	-
HR50	12				655	310	-	-	-	-	-	-	-	-	-	-	-	-	0
					95	45	-	-	-	-	-	-	-	-	-	-	-	-
	25-Dec				655	310	-	-	-	-	-	-	-	-	-	-	-	-	0
	0.98 - 1.97				90	43	-	-	-	-	-	-	-	-	-	-	-	-
	25 - 50				620	295	-	-	-	-	-	-	-	-	-	-	-	-	0
	1.97 - 3.15				90	40	-	-	-	-	-	-	-	-	-	-	-	-
	50 - 80				620	275	-	-	-	-	-	-	-	-	-	-	-	-	0
M20	3.15 - 4.92				90	35	-	-	-	-	-	-	-	-	-	-	-	-
M20	80 - 125				620	240	-	-	-	-	-	-	-	-	-	-	-	-	0

PHYSICAL PROPERTIES

Product Property	US Customary	Metric
Coefficient of Thermal Expansion	9.0 ·10-6 per oF (68-572 F)	16.2 ∙ 10 6ֿ per ˚C (20-300 C)
Density	0.269 lb/in3 at 68 F	7.45 gm/cm3 @ 20 C
Electrical Conductivity	12 %IACS @ 68 F	0.07 MegaSiemens/cm @ 20 C
Electrical Resistivity	86.4 ohms-cmil/ft @ 68 F	14.36 microhm-cm @ 20 C
Melting Point Liquid US	1900 F	1038 C
Melting Point Solid US	1880 F	1027 C
Modulas of Elasticity in Tension	17000 ksi	117000 MPa
Modulas of Rigidity	6400 ksi	44130 MPa
Specific Gravity	7.45	7.45
Specific Heat Capacity	0.09 Btu/lb/˚F @ 68 F	377.1 J/kg ∙ ˚K at 293 K
Thermal Conductivity	34.0 Btu ∙ ft/(hr ∙ ft2 ∙˚F) @ 68 F	58.8 W/m ∙ ˚K at 20 C

FABRICATION

Joining Technique	Suitability
Brazing	Fair
Butt Weld	Good
Capacity for Being Cold Worked	Poor
Capacity for Being Hot Formed	Excellent
Coated Metal Arc Welding	Good
Forgeability Rating	80
Gas Sheilded Arc Welding	Good
Machinability rating	50
Oxyacetylene Welding	Not Recommended
Seam Weld	Good
Soldering	Not Recommended
Spot Weld	Good

SPECIFICATIONS

End Product	Specification
Forgings	SAE J463, J461
Rod	ASTM B150
Rod, Welding	AWS A5.7